Technical features
Rust protection for metal parts machined with the tool in the interval between the machining of finished metal objects for storage after sandblasting or lapping. Protective of machinery, including the food industry, during off seasons. FIPRO DK 406 is suitable for “Indoor” protection.
Tests carried out at a relative humidity of 95% + 2% and at 49 ° C have shown that the film left by FIPRO DK 406 protects clean or sandblasted iron surfaces from oxidation for 30 days.
The surfaces treated with FIPRO DK 406 are clean and dry.
Physical-Chemical Data
Parametro | Valore |
|---|---|
Appearance | Amber liquid |
Density at 20 °C | 1.090 ± 0.01 g/ml |
Specific Weight at 20 °C | 0.83 Kg/lt |
Foam formation | Low |
Usage and Applications
FIPRO DK 406 is applied by immersion, brush or spray (not atomised).
For a better protective effect, the metal parts must be cleaned and rinsed before treatment.
In cases where a lower protection is sufficient, it can be diluted up to 50%. By volume with white spirit or Kerosene. The protective film can be removed with alkaline degreasers or the solvent type. With 4 liters of product, 3-12 m2 of surface can be treated according to the method of application, temperature and porosity of the metal.
Drying in a ventilated oven at low temperature, or by evaporation of the solvent at room temperature.
Applicazione | Concentrazione |
|---|
Plant
The containment tanks must be constructed of iron and with a conical or inclined bottom, equipped with a drain valve to eliminate the water that builds up on the bottom. The analytical control of the product is not foreseen. Feed according to the level.